Comparative Study of 2060-T8 Al-Li Alloy Friction Stir Welded Joints Between Natural Cooling and Water Cooling

Comparative Study of 2060-T8 Al-Li Alloy Friction Stir Welded Joints Between Natural Cooling and Water Cooling

Blog Article

2060-T8 Al-Li alloy was friction stir butt welded under natural and water cooling conditions.Microstructures and mechanical properties of the welding joints were mainly compared and discussed.By spraying water on the top surface of stir zone, the grain size was reduced, attributing to the improvement of microhardness.

The maximum tensile strength under the ucsb gaucho blue water cooling reached 461.1 MPa.The joint fractured at the stir zone due to the thickness reduction and the 100w products joint softening.

The fracture surface consisted of many dimples with various sizes, indicating the typical ductile fracture.The strategy to apply the low heat input at the welding stage and high cooling rate at the cooling stage during FSW is necessary to obtain a high-quality FSW joint.